Solvoxy (L1); SSPL/EPOXY - MB (L1) ScopeA two pack self priming air-drying High Build Polyamine adducts cured Epoxy coating. Areas of ApplicationsAn ideal tank lining for fresh & salt water, brine, sweet and sour crude and other refined petroleum products and solvents.
For lining potable water tanks. Technical DataProduct | 455 | Colour & Gloss | As recommended – Matt | Mixing Ratio | Base: Hardener 4:1 (By volume) | Maturation time | 40 minutes | Pot life of mixture | 3 hours at 300C | Recommended DFT
| On Brushing | 75 Microns per coat | On Airless Spray | 100 Microns per coat | Covering Capacity (Theoretical) | 8.0 sq.mtr/ltr. at 75 microns DFT
6.0 sq.mtr/ltr. at 100 microns DFT | Method of Application | Brush/Airless Spray | Thinner Recommended | Brushing/Airless Spray: 0-5% | Drying Time | Surface Dry: 2 hours at 300C | | Hard Dry: 16 Hours at 300C | Recoating Period | Min. 16 hours | | Max. 48 hours | Packs Offered | 20 litres | | Storage & HandlingStorage | Store in a cool dry place | Shelf Life | Minimum 12 months, provided components are unmixed and stored in a sealed containers | Disposal | Dispose in land filling and not in drain or any water channel | | Directions for Usesurface preparation
Blast clean Mild steel substrate to Sa 2 ½ of Swedish specifications SIS-05-5900-1967 or near white metal of IS specifications IS 1477-1971 (Part I).
No other mode of surface preparation other than blast cleaning is permissible.
If desired suitable Epoxy Primer or Inorganic Zinc Silicate Primer can be used. Special InstructionFor getting best results, apply three coats at 75 microns by brush or two coats of 100 microns by airless spray.
Minimum 7 days curing shall be provided before coating is subjected for immersion conditions. Safety InformationFlash Point | Not below 210C | Fire Hazard ClassS | Flammable | Safety Precaution | Work in well ventilated place. Wear protective clothing like overalls and gloves. Please refer to our Safety Data Sheet | | |