Nominal Thickness | 2000 microns |
Tensile strength as per ASTM D – 638 | 17 N/mm2 Min. |
Adhesion ASTM D – 4541 | 8 N/mm2 Min. |
Recoverable elongation as per ASTM D 638 | 50% Min. |
Surface Hardness, ASTM D 2240 | 50 Min. shore D |
Water vapour permeability as per ASTM E-96/F-1249/90 | 0.3 gms/24 hrs/m2 Max. |
Operating Temperatures | 0°C to 60°C |
Salt spray test 6000 hours, ASTM B 117-73 | No effect |
Impact resistance as per
ASTM D 1737 ASTM G – 14 | 0.23 x 106 gm – cm. min.
200 inch – Lb –Min. |
Abrasion Resistance ASTM D 4060/FTMS 141
Taker abraser H-10 wheel 1000 gms, 1000 cycles | Weight Loss 0.05 gms. Max
|
Flexibility as per ASTM D 1737 | No effect pass over 12 mm mandrel 180° Bend- 0.5 mm thick plate coated with 0.5 mm thick coating |
Accelerated weathering ASTM G – 53/BS 3800
2000 hours | No effect expect some
Discoloration |
Chemical Resistance:
Immersion of 30 days in Sea water followed by
(%) Weight
(%) Hardness (Shore D) Change
(%) Tensile Strength change |
<1.0%
<5.0%
<5.0% |